Filled UHMW’s and Properties
| Property | Units | Test Method | Poly-Texx 1000 | Poly-Texx XL | Poly-Texx AR | Poly-Texx MPG | Poly-Texx R | Poly-Texx M | Poly-Texx MX |
| *(Unverified / Verbal Information) | (Virgin UHMW) | Cross Linked | Proprietary Filled UHMW | Glass Bead Filled UHMW | Reprocessed UHMW | Heat Stabilized (HOT) | Heat Stabilized Internally Lubricated | ||
| Average Cost Per SF of 1" Thick" | U.S. Dollar | 1"x12"x12" | $20.00 | $32.00 | $43.00 | $32.00 | $16.00 | $40.00 | $32.00 |
| Specific Gravity | ASTM D-792 | 0.94 | 0.94 | .932-.96 | 0.96 | 0.94 | 0.93 | 0.95-96 | |
| Tensile Strength at Yield | psi | ASTM D-638 | 3100 | 2900 | 2700-2900 | 2,700 | 3000 | 2600-3200 | >3200 |
| Tensile Elongation at Yield | % | ASTM D-638 | 350 | 300 | 350 | >290 | >290 | ||
| Tensile Strength at Break | psi | ASTM D-638 | 350 | 300 | 4,600-6,800 | 4,800-5,800 | 4,800-5,800 | ||
| Tensile Elongation at Break | % | ASTM D-638 | 350 | 350 | >300 | 300 | 350 | 350 | 350 |
| Tensile Modulus | psi | ASTM D-638 | |||||||
| Flexural Modulus | psi | ASTM D-790 | 100,000-150,000 | 100,000-150,000 | 100,000-150,000 | 100,000-150,000 | 100,000-150,000 | ||
| Notched Izod Impact | ft lbs/in2 | ASTM D-4020 | 125 | 125 | No Break | No Break | No Break | No Break | |
| Izod Impact Double Notched | ft lbs/in2 | ASTM D-256 | No Break | No Break | 25 | 24 | >20 | >20 | >20 |
| Tensile Impact | ft lbs/in2 | DIN 53488 | |||||||
| Sand Wheel Wear | T=1000=100 | ASTM G-65 | 100 | 100 | 120 | 110 | 100 | 100 | 85 |
| Hardness, Shore D | D Scale | ASTM D-2240 | 62-67 | 62-67 | |||||
| Hardness, Rockwell | R Scale | ASTM D-785 | 62-66 | 62-67 | 62-66 | 62-67 | 62-66 | ||
| Coefficient of Friction-Static | ASTM D-1894 | .15-.2 | .15-.2 | .12-.15 | .15-.20 | .17-.2 | .15-.2 | .10-.15 | |
| Coefficient of Friction-Dynamic | ASTM D-1894 | .10-.2 | .10-.2 | .07-.10 | .10-.12 | .10-.2 | .10-.15 | .07-.10 | |
| Coefficient of Linear Thermal Expansion | in/in/deg F | ATM D-696 | 1.1xE-4 | .55xE-4 | 1.0xE-4 | 1.0xE-4 | .95xE-4 | .55xE-4 | .50xE-4 |
| Melting Point | Degree F | ASTM D-3417 | 280 | 280 | 275-280 | 275-280 | 280 | 280 | 280 |
| Softening Point | Degree F | 180 | |||||||
| Continuous Service Temperature | Degrees F | 180 | 180 | 180 | 180 | 180 | 350 | 180 | |
| Intermittent Service Temperature | Degrees F | 200 | 200 | 200 | 200 | 200 | 350 | 200 | |
| Compressive Strength @ 72F | psi | LVF1297 | 800 | 800 | 1,000 | 1,000 | 850 | 600 | 800 |
| Compressive Modulus | psi | ASTM D-621 | |||||||
| Compressive Deformation Under Load | % @ 1000psi | ASTM D-621 | 2-5% | 2-5% | 2% | 2% | 2-5% | 2-5% | 2-5% |
| Flexural Strength | psi | ASTM D-790 | |||||||
| Shear Strength | psi | ASTM D-732 | |||||||
| Dielectric Strength (Short Time) | Volts/mil | D-149 | 2,300 | 2,300 | 900 | 2,300 | 2,300 | 2,300 | |
| Dielectric Constant | ASTM D-150 | ||||||||
| @60 cycles | |||||||||
| @1000 cycles | @1KHz | D-150 | 2.3 | 2.3 | 2.3 | 2.3 | 2.3 | 2.3 | |
| @100,000 cycles | |||||||||
| Volume Resistivity | Ohm/cm | ASTM D-257 | >10xE15 | 10xE15 | 10xE15 | 10xE15 | 10xE15 | 10xE15 | |
| Surface Resistivity | Ohm | ASTM D-257 | 10xE6 | 10xE6 | |||||
| Water Absorption | % | ASTM D-5706 | nil | nil | nil | nil | nil | nil | nil |
| 24 Hours | % | ASTM D570 | nil | nil | nil | nil | nil | nil | nil |
| Saturation | % | ASTM D570 | nil | nil | nil | nil | nil | nil | nil |